2. nickel-chromium-iron-molybdenum-copper alloy rods (UNS N06007, N06975, N06985, N06030, and N08031), hot- or cold-finished, solution annealed, ground, or turned, for use in general corrosive service
|
Element
|
Composition Limits, %
|
|
|
Alloy N06007
|
Alloy N06975
|
Alloy N06985
|
Alloy N06030
|
Alloy N08031
|
|
Nickel
|
remainder
|
47.0–52.0
|
remainder
|
remainder
|
30.0-32.0
|
|
Chromium
|
21.0–23.5
|
23.0–26.0
|
21.0–23.5
|
28.0–31.5
|
26.0-28.0
|
|
Iron
|
18.0–21.0
|
remainder
|
18.0–21.0
|
13.0–17.0
|
remainder
|
|
Molybdenum
|
5.5–7.5
|
5.0–7.0
|
6.0–8.0
|
4.0–6.0
|
6.0-7.0†
|
|
Copper
|
1.5–2.5
|
0.70–1.20
|
1.5–2.5
|
1.0–2.4
|
1.0-1.4
|
|
Manganese
|
1.0–2.0
|
1.0 max
|
1.0 max
|
1.5 max
|
2.0 max
|
|
Cobalt, max
|
2.5
|
...
|
5.0 max
|
5.0 max
|
...
|
|
Carbon, max
|
0.05
|
0.03
|
0.015 max
|
0.03 max
|
0.015
|
|
Tungsten
|
1.0 max
|
...
|
1.5 max
|
1.5–4.0
|
...
|
|
Silicon, max
|
1.0
|
1.0
|
1.0 max
|
0.8 max
|
0.3
|
|
Phosphorus, max
|
0.04
|
0.03
|
0.04 max
|
0.04 max
|
0.020
|
|
Sulfur, max
|
0.03
|
0.03
|
0.03 max
|
0.02 max
|
0.010
|
|
Columbium + tantalum
|
1.75–2.50
|
...
|
0.50 max
|
0.30–1.50
|
...
|
|
Titanium
|
...
|
0.7–1.5
|
...
|
...
|
...
|
|
Nitrogen
|
0.15-0.25
|
...
|
...
|
...
|
...
|
|
Alloy
|
Specified Diameter, in. (mm)
|
Tensile Strength min, psi (MPa)
|
Yield Strength (0.2 % Offset), min, psi (MPa)
|
Elongation in 2 in. or 50.8 mm or 4D min
|
|
N06007
|
5/16 to 3/4 (7.94 to 19.05), incl
|
90 000 (621)
|
35 000 (241)
|
35
|
|
|
Over 3/4 to 31/2 (19.05 to 88.9), incl
|
85 000 (586)
|
30 000 (207)
|
30
|
|
N06975
|
5/16 to 31/2 (7.94 to 88.9), incl
|
85 000 (586)
|
32 000 (221)
|
40
|
|
N06985
|
5/16 to 3/4 (7.9 to 19.05), incl
|
90 000 (621)
|
35 000 (241)
|
45
|
|
|
Over 3/4 to 31/2 (19.05 to 88.9), incl
|
85 000 (586)
|
30 000 (207)
|
35
|
|
N06030
|
...
|
85 000 (586)
|
35 000 (241)
|
30
|
|
N08031
|
All sizes
|
94 000 (648)
|
40 000 (276)
|
40
|
----------Accept The 3rd Party (SGS/TUV/BV, etc) TO TEST
3. size 7.94~88.9mm diameter
4. surface pickled,Lathe polished,descaling,black,bright, acid-producing white,drawn-bright
5. Packing: steel strip or wooden cases
6. Lead time: 10~30days according to qty
7. Test: in-house or the 3rd party to test (SGS,TUV,BV,etc)